| Yazarlar (2) |
Fatih Yapıcı
Ondokuz Mayıs Üniversitesi, Türkiye |
Doç. Dr. Raşit ESEN
Karabük Üniversitesi, Türkiye |
| Özet |
| This study was carried out to determine the effects of pres time and pres pressure on modulus of rupture (MOR) and modulus of elasticity (MOE) properties of oriented strand board (OSB). For this purpose, 80 mm long strands made of poplar wood bonded with phenol-formaldehyde resin at (9 %) with three-layer cross-aligned OSBs. The strands used for the production of test panels were made up 50 % of core layer and 50 % of outer layers. The panels were pressed for three different press times, from 3, 6 to 9 minutes, using 30, 40 and 50 kg/cm2 bar pressure respectively, aimed for density of 0.65 g/cm3. |
| Anahtar Kelimeler |
| MOE value | MOR value | Oriented strand board | Phenol-formaldehyde |
| Bildiri Türü | Tebliğ/Bildiri |
| Bildiri Alt Türü | Tam Metin Olarak Yayımlanan Tebliğ (Uluslararası Kongre/Sempozyum) |
| Bildiri Niteliği | Alanında Hakemli Uluslararası Kongre/Sempozyum |
| Bildiri Dili | İngilizce |
| Kongre Adı | 24th İnternational Scientific Conference October 2013 |
| Kongre Tarihi | 18-10-2013 / 18-10-2013 |
| Basıldığı Ülke | Hırvatistan |
| Basıldığı Şehir | Zagrap |