Mohamed Ahmed Ahssi
Türkiye |
Prof. Dr. Mehmet Akif ERDEN
Karabük Üniversitesi, Türkiye |
|
Mustafa Acarer
Selçuk Üniversitesi, Türkiye |
Doç. Dr. Harun ÇUĞ
Karabük Üniversitesi, Türkiye |
| Özet |
| In this study, the effects of adding Ni in different ratios to Fe-matrix material containing C-Nb-V produced by powder metallurgy on microstructure, tensile strength, hardness and corrosion behaviors were investigated. Fe-C and Fe-C-Nb-V powders containing 5%, 10%, 13%, 15%, 20%, 30% and 40% nickel were pressed at 700 MPa and then sintered in an Ar atmosphere at 1400 °C. Microstructures of the samples were characterized with optical microscope, scanning electron microscope (SEM) and XRD. Corrosion behaviors were investigated by obtaining Tafel curves in an aqueous solution containing 3.5% NaCl. Mechanical properties were determined by hardness and tensile testing. While Fe-C alloy and Fe-C-Nb-V microalloyed steel without Ni typically have a ferrite-pearlite microstructure, the austenite phase has been observed in the microstructures of the alloys with 10% nickel and further. Yield and tensile strength increased with nickel content and reached the highest strength values with 13% Ni content. The addition of more nickel led to decrease the strength. Analysis of Tafel curves showed that corrosion resistance of alloys increased with increasing nickel concentration. |
| Anahtar Kelimeler |
| Corrosion | Mechanical properties | Microalloyed steel | Microstructure | Nickel addition | Powder metallurgy |
| Makale Türü | Özgün Makale |
| Makale Alt Türü | SSCI, AHCI, SCI, SCI-Exp dergilerinde yayımlanan tam makale |
| Dergi Adı | MATERIALS |
| Dergi ISSN | - |
| Dergi Tarandığı Indeksler | SCI-Expanded |
| Dergi Grubu | Q2 |
| Makale Dili | İngilizce |
| Basım Tarihi | 09-2020 |
| Cilt No | 13 |
| Sayı | 18 |
| Sayfalar | 4021 / 0 |
| Doi Numarası | 10.3390/ma13184021 |
| Atıf Sayıları | |
| WoS | 32 |
| SCOPUS | 39 |
| Google Scholar | 54 |