| Özet |
| This study analyzes how hot rolling changes microstructure, tensile strength, wear, and corrosion behavior of Fe-0.55C3Mo-10Ni-0.5W alloy steel. The metal powders were pressed at 750 MPa pressure, and the cold-pressed samples were sintered for two hours at 5°C/min up to 1400°C in a mixed-gas environment of 90% nitrogen and 10% hydrogen. The steels produced were then hot rolled at 40% and 80% deformation rate. The microstructures demonstrate that MoC(N), WC(N), and MoWC(N) were produced and that the steels exhibited finer microstructures and better mechanical properties as the deformation rate increased. Wear decreased as the deformation rate increased. Furthermore, the the hot rolling method improved the corrosion resistance, as shown by the Tafel curve analysis. The greatest factor supporting the corrosion resistance was the increase in density value throughout the rolling process. |
| Anahtar Kelimeler |
| Alloy steels | Characterization | Corrosion | Habanje | Hot rolling | Karakterizacija | Korozija | Legirani čelici | Metalurgija praha | Powder metallurgy | Toplo valjanje | Wear |
| Makale Türü | Özgün Makale |
| Makale Alt Türü | SSCI, AHCI, SCI, SCI-Exp dergilerinde yayımlanan tam makale |
| Dergi Adı | Journal of Mining and Metallurgy, Section B: Metallurgy |
| Dergi ISSN | 1450-5339 Wos Dergi Scopus Dergi |
| Dergi Tarandığı Indeksler | SCI-Expanded |
| Dergi Grubu | Q3 |
| Makale Dili | İngilizce |
| Basım Tarihi | 12-2024 |
| Cilt No | 60 |
| Sayı | 3 |
| Sayfalar | 367 / 380 |
| Doi Numarası | 10.2298/JMMB240404030E |
| Makale Linki | https://doi.org/10.2298/jmmb240404030e |
| Atıf Sayıları | |
| WoS | 1 |
| SCOPUS | 1 |
| Google Scholar | 1 |