| Yazarlar (5) |
Prof. Dr. Fatma MEYDANERİ TEZEL
Karabük Üniversitesi, Türkiye |
B. Saatçi
Erciyes Üniversitesi, Türkiye |
|
M. Ari
Erciyes Üniversitesi, Türkiye |
|
S. Durmuş Acer
Dumluplnar University, Türkiye |
|
E. Altuner
Erciyes Üniversitesi, Türkiye |
| Özet |
| The structural, surface and transport properties of Sn-Ag alloys were investigated by X-ray diffraction (XRD), radial heat flow, energy-dispersive X-ray (EDX) analysis, scanning electron microscopy (SEM) and four-point probe techniques. We observed that the samples had tetragonal crystal symmetry except for the pure Ag sample which had cubic crystal symmetry, and with the addition of Ag the cell parameters increased slightly. Smooth surfaces with a clear grain boundary for the samples were shown on the SEM micrographs. The grain sizes of pure Ag, β-Sn and the formed Ag3Sn intermetallic compound phase for Sn-x wt.% Ag [x=1.5, 3.5] binary alloys were determined to be 316nm, between 92nm and 80nm and between 36nm and 34nm, respectively. The values of electrical resistivity for pure Sn, pure Ag and Sn-x wt.% Ag [x=1.5, 3.5] were obtained to be 22.60×10-8, 62.36×10-8, 23.54×10-8, 24.62×10-8Ωm at the temperature range of 300-450K, respectively. Thermal conductivity values of pure Sn and Sn-x wt.% Ag [x=1.5, 3.5] binary alloys were found to be 60.60±3.75, 69.00±4.27 and 84.60±5.24W/Km. These values slightly decreased with increasing temperature and increase with increasing of the Ag composition. Additionally, the temperature coefficients of thermal conductivity and electrical resistivity and the Lorenz numbers were calculated. |
| Anahtar Kelimeler |
| Electrical resistivity | grain size | radial heat flow | surface properties |
| Makale Türü | Özgün Makale |
| Makale Alt Türü | SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale |
| Dergi Adı | SURFACE REVIEW AND LETTERS |
| Dergi ISSN | 0218-625X Wos Dergi Scopus Dergi |
| Dergi Tarandığı Indeksler | SCI |
| Dergi Grubu | Q4 |
| Makale Dili | İngilizce |
| Basım Tarihi | 03-2017 |
| Cilt No | 24 |
| Sayı | 3 |
| Sayfalar | 1750033 / 17500146 |
| Doi Numarası | 10.1142/S0218625X17500330 |
| Atıf Sayıları | |
| WoS | 2 |
| SCOPUS | 2 |
| Google Scholar | 2 |
| Google Scholar | 10 |